铁锈对介质损耗值测量的影响及其电阻特性分析 

徐炎斌，吴祖现 
(广东电网有限责任公司江门供电局，广东 江门 529000) 
 

摘 要： 介质损耗因数是判断电力设备绝缘性能的重要依据，分析了接触不良导致的介质损耗因数测量值偏大的原因。通过试验，对比了铁锈和不同阻值碳膜电阻对介质损耗测量的影响差异。结果表明，不同试验电压下，铁锈表现出与碳膜电阻不一样的电阻特性。
关键词： 铁锈；接触电阻；介质损耗因数；绝缘电阻
中图分类号：TM835.4 文献标识码：B 文章编号：1007-3175(2015)05-0041-03

Influence of Rust on Measurement of Dielectric Loss and Its Resistance Characteristic Analysis 

XU Yan-bin, WU Zu-xian 
（Jiangmen Power Supply Bureau of Guangdong Power Grid Co., Ltd, Jiangmen 529000, China） 
 

Abstract: The dielectric loss factor is the important basis to judge insulating property of electrical equipment. This paper analyzed the reason of the test value of bigger dielectric loss factor caused by bad contact. Via the simulation test, effect on the test results between rust and different carbon film resistors was compared. The result shows that under different test voltage, the resistor characteristic of rust is different from that of carbon film resistor.
Key words: rust; contact resistance; dielectric loss factor; insulation resistance

参考文献
[1] 陈天翔，王寅仲，海世杰.电气试验[M].2版.北京：中国电力出版社，2008.
[2] 李顺尧.220 kV电容式电压互感器试验方法探讨[J].高压电器，2008，44(3)：280-282.
[3] 左文启，葛广勇，叶洪波.220 kV CVT不拆高压引线现场测试新方法[J].高压电器，2010，46(8)：72-75.
[4] 马杰聪.变频介损仪在电容式电压互感器不拆线试验中的应用[J].科技信息，2010(5)：724-726.
[5] 马明，戴瑞海，林坚. 耦合电容器不拆高压引线试验方法研究[J]. 电力电容器与无功补偿，2010，31(2)：36-38.
[6] 廖肇毅.简述500 kV电容式电压互感器不拆线预试方法[J].广东输电与变电技术，2010(2)：37-38.
[7] 胡伟涛. 提高不拆线测量500 kV CVT 介损及电容量准确度的方法[J]. 电力电容器与无功补偿，2011，32(6)：69-73.
[8] 李涛，杜晓平，陈瑞林.电容型电流互感器现场试验tanδ值异常的分析及解决方法[J].电力系统保护与控制，2009，37(20)：120-122.
[9] 古国榜，李朴.无机化学[M].2版.北京：化学工业出版社，2009.